We are certified company, engaged in offering supreme quality assortment of Anviloy for Die Casting. Through the hand of deft professionals, this is manufactured using premium quality materials and advanced techniques. Due to its unique temper resistance properties and good thermal conductivity, this item can easily eliminate heat and lowers the possibilities of heat cracks and soldering effect. Moreover, we are offering this Anviloy for Die Casting in several sizes at industry leading prices.
Features:
- Robust construction
- High strength
- Easy installation
- Exceptional erosion and rust prevention capacity
- Its strength and hardness remain intact even under high temperature. Thus, it ensures its dimensional stability
- Good machinability
- Lowers release angles
Application
- Hot runner nozzles
- Shot sleeves
- Vibration and tool chatter reduction
- Plastic injection molding
- Extrusion dies
- Die cast tooling
Technical Specification :
ANVILOY Special Alloys for Die Casting :
|
| Density | UTS Rm | Elongation | Youngâââ¬Ã¢â¢s Modulus | Hardness | Resistance (300K) | Heat Conductivity ÃŽû (300K) |
|
| g/cmÃâó | MPa | % | GPa | HV10 | ÃŽüÃŽéâÃâ ââ¢cm | W/(m. K) |
| Anviloỷ̨1050 | 17,0 | 900 | > 20 | 330 | 300 | na | 70 |
| Anviloỷ̨1150 | 17,3 | 950 | > 10 | 360 | 350 | na | 90 |
| Anviloỷ̨1350 | 18,5 | 800 | > 10 | 370 | 310 | 10 | 65 |
| Anviloỷ̨ Weld Rod | na | na | na | na | na | na | na |
According SAE: AMS-T-21014, ASTMB777,AMS 7725
Anviloy 1150 vs H-13
Typical Mechanical Properties at Room Temperature :
|
| Anviloy 1150 | H-13 |
| Ultimate Tensile Strength, psi(MPa) | 140000(965) | 233000(1610) |
| Yield Strength, 0.2%offset, psi(MPa) | 125000(862) | 192000(1320) |
| Elongation, % in 2 inches | 3.0 | 13.1 |
| Hardness, HRC | 34 | 45 |
| Modulus of Elasticity, psiââ¬â106(GPa) | 49.0 (338) | 30.5 (210) |
Tensile Properties at Elevated Temperature :
|
| Anviloy 1150 | H-13 |
| UTS, psi(MPa)at 1000oF(537oC) | 113000 (779) | 142000 (979) |
| UTS, psi(MPa)at 1200oF(648oC) | 105000 (724) | 85000 (586) |
| UTS, psi(MPa)at 1500oF(815oC) | 75000 (517) | 20500 (141) |
Coefficient of Thermal Expansion :
| 68-750oF(20-400oC) | 2.52x10-6(4.54x10)-6 | 6.8x10-6(12.2x10)-6 |
| 68-1450oF(20-790oC) | 2.92x10-6(5.26x10)-6 | 7.5x10-6(13.5x10)-6 |
| Thermal Conductivity [W/m.K] 500oC | 70.2 | 28.4 |
| Density, ib/in3(g/cm3) | 0.623(17.25) | 0.280(7.76) |